C1300H
Carbon-fiber-reinforced injection-molding grade of polyamide 9T (PA9T). In addition to low water absorption and dimensional stability, it offers high strength, making it suitable for gears and various structural parts.
CF reinforced
Standard
Application examples
gears, retainers
Property table
| Unit | Test method | Value | |
|---|---|---|---|
| Grade name | C1300H | ||
| carbon fiber content | ％ | ― | 30 |
/
Physical properties
| Specific gravity | - | ISO 1183 | 1.27 |
| Water absorption (23°C, immersed in water for 24hrs) | ％ | ISO 62 | 0.2 |
/
Mechanical properties
| Tensile strength | MPa | ISO 527 | 260 |
| Flexural strength | MPa | ISO 178 | 385 |
| Flexural modulus | GPa | ISO 178 | 20 |
| Charpy notched impact strength | kJ/m2 | ISO 179/1eA | 7.5 |
/
Thermal properties
| Melting point | ℃ | ISO 11357-3 | 305 |
/
Dimensional properties
| Mold shrinkage (2 mmt), flow direction | ％ | ISO 294-4 | 0.0 |
| Mold shrinkage (2 mmt), transverse direction | ％ | ISO 294-4 | 0.5 |
/
* The above data are property values measured in the absolutely dry state.
* The above data are actual measured values obtained by our company and are not guaranteed values.