G1350A-M32T
Reinforced injection-molding grade of polyamide 9T (PA9T). Thanks to our proprietary compounding technology, it offers low water absorption, dimensional stability, heat resistance, and chemical resistance, as well as excellent laser-marking properties, making it suitable for a wide range of automotive and industrial components.
Reinforced
Laser transparency
Application examples
Property table
| Unit | Test method | Value | |
|---|---|---|---|
| Grade name | G1350A-M32T | ||
| Glass fiber content | ％ | ― | 35 |
/
Physical properties
| Specific gravity | - | ISO 1183 | 1.40 |
| Water absorption (23°C, immersed in water for 24hrs) | ％ | ISO 62 | 0.19 |
/
Mechanical properties
| Tensile strength | MPa | ISO 527 | 195 |
| Flexural strength | MPa | ISO 178 | 275 |
| Flexural modulus | GPa | ISO 178 | 10 |
| Charpy notched impact strength | kJ/m2 | ISO 179/1eA | 12 |
/
Thermal properties
| Melting point | ℃ | ISO 11357-3 | 300 |
/
Dimensional properties
| Mold shrinkage (2 mmt), flow direction | ％ | ISO 294-4 | 0.3 |
| Mold shrinkage (2 mmt), transverse direction | ％ | ISO 294-4 | 0.9 |
/
* The above data are property values measured in the absolutely dry state.
* The above data are actual measured values obtained by our company and are not guaranteed values.