N1001A
Unreinforced injection-molding grade of polyamide 9T (PA9T). It offers excellent low water absorption, dimensional stability, heat resistance, and chemical resistance, along with superior sliding properties, making it suitable for gears, cable ties, and other automotive and industrial applications.
High slidability
Application examples
Property table
| Unit | Test method | Value | |
|---|---|---|---|
| Grade name | N1001A | ||
| Glass fiber content | ％ | ― | 0 |
/
Physical properties
| Specific gravity | - | ISO 1183 | 1.11 |
| Water absorption (23°C, immersed in water for 24hrs) | ％ | ISO 62 | 0.25 |
/
Mechanical properties
| Tensile strength | MPa | ISO 527 | 80 |
| Flexural strength | MPa | ISO 178 | 105 |
| Flexural modulus | GPa | ISO 178 | 2.3 |
| Charpy impact strength with a notch | kJ/m2 | ISO 179/1eA | 9 |
/
Thermal properties
| Melting point | ℃ | ISO 11357-3 | 300 |
/
Dimensional properties
| Mold shrinkage (2 mmt), flow direction | ％ | ISO 294-4 | 1.4 |
| Mold shrinkage (2 mmt), transverse direction | ％ | ISO 294-4 | 1.5 |
/
*The above data are property values measured in the absolutely dry state.
*The above data are actual measured values obtained by our company and are not guaranteed values.