N1006A
Unreinforced injection-molding grade of polyamide 9T (PA9T). It offers excellent low water absorption, dimensional stability, heat resistance, and chemical resistance, together with high impact resistance and flexibility, making it suitable for joint parts, cable ties, and other automotive and industrial applications.
High toughness
Application examples
Physical properties table
| Units | Test method | Value | |
|---|---|---|---|
| Grade name | N1006A | ||
| Glass fiber content | ％ | ― | 0 |
/
Basic physical properties
| Specific gravity | - | ISO 1183 | 1.06 |
| Water absorption rate(23℃ in water, 24hrs) | ％ | ISO 62 | 0.25 |
/
Mechanical properties
| Tensile strength | MPa | ISO 527 | 50 |
| Flexural strength | MPa | ISO 178 | 70 |
| Flexural modulus | GPa | ISO 178 | 1.5 |
| Charpy impact strength with a notch | kJ/m2 | ISO 179/1eA | 65 |
/
Thermal properties
| Melting point | ℃ | ISO 11357-3 | 300 |
/
Dimensional properties
| Mold shrinkage(2mmt) :in direction of flow | ％ | ISO 294-4 | 1.4 |
| :at right angles to flow | ％ | ISO 294-4 | 1.5 |
/
＊The above data are the physical values measured at the absolute dry condition.
＊The above data are values measured by our company and do not guarantee performance.